Name | Core Material | Surface Modification | PPS | Surface Area (BET) | Agglomerate Size in F12K (z.average) | Zeta Potential |
---|---|---|---|---|---|---|
 |  |  | [nm] | [m2/g] | [nm] | [mV] |
SiO2_15_Unmod | Silica | None | 15 | 200 | 42 | −35.5 |
SiO2_15_Phospho | Phosphonate | 15 | 200 | 93 | − 42.3 | |
SiO2_15_Amino | Amino | 15 | 200 | 144 | −30.9 | |
SiO2_40 | None | 40 | 50 | 255 | − 38.8 | |
SiO2_7 | None | 8 | 300 | 275 | −26.6 | |
SiO2_7_TMS2 | 2% TMS | 8 | 300 | 159 | −1.0 | |
SiO2_7_TMS3 | 3% TMS | 8 | 300 | 403 | −8.8 | |
TiO2_NM105 | Titanium dioxide | None | 21 | 51 | 3490 | −16.5 |
Graphene Oxide | Graphene oxide | None | – | – | 1927 | −16.2 |
Phthalocyanine Blue | Cu-phthalo-cyanine Halogenated Cu-phathalo-cyanine | None | 17 | 53 | 1760 | −24.1 |
Phthalocyanine Green | None | – | 69 | 1784 | −37.0 | |
Mn2O3 | Manganese oxide | None | 50 | 19.9 | 676 | −24.6 |